| Bi-metal Cladding Steel Pipe |
Bi-metal Clad Pipe and Bend are cast with mold vanishing vacuum suction casting cladding process. Outer of straight pipe is common steel pipe, cladding realized by forming high chromium lining via centrifugal forming technique.
1. Manufacturing Process of Bimetal Clad Pipe and Bend:
Bimetal Clad Pipe and Bend are cast with mold vanishing vacuum suction casting cladding process. Outer of straight pipe is common steel pipe, cladding realized by forming high chromium lining via centrifugal forming technique. Outer of bend uses hot-bending bend and lining is cast with high-chromium cast iron. Bends and other profile sections can be cladded in whole and this process has changed the traditional practice to fabricate bend and other profile sections by drawing polyline without changing flow pattern of material inside piping,greatly reducing conveyance resistance of material.2. Advantages Compared with Traditional Wear Resistant
Alloy Cast Iron, Alloy Cast Steel, General Clad Steel Pipe and Cast Stone Pipe:
1. Good wear-resistance, giving full play to wear-resistance of high chromium cast iron.
2. Withstanding high pressure:
Bimetal cladding pipe and bend can be used for any pressure rating. Close bonding of outer and lining by adopting special process make cladding interlayer molten-joint to ensure reliable operation.
3. Good mechanical impact and thermal impact resistance property.
4. Convenient in connection for installation:
Bimetal cladding pipe and bend can be cut and welded as you like.
1. Good wear-resistance, giving full play to wear-resistance of high chromium cast iron.
2. Withstanding high pressure:
Bimetal cladding pipe and bend can be used for any pressure rating. Close bonding of outer and lining by adopting special process make cladding interlayer molten-joint to ensure reliable operation.
3. Good mechanical impact and thermal impact resistance property.
4. Convenient in connection for installation:
Bimetal cladding pipe and bend can be cut and welded as you like.
3. Physical Properties of Bimetal Clad Pipe and Bend:
| Flexure Strength | Tensile Strength | Elongation | Cross Section Stretch Ratio | Impact Toughness | Hardness of Wearable Layer | Hydrostatic Testing Pressure |
MN/㎡ | MN/㎡ | % | % | J/c㎡ | HRC | Mpa |
| >610 | >700 | 5 | 5.1 | >15 | >38 | 5.6-12.9 |